    Síntesis y caracterización de heteropolioxometalatos tipo anderson de Ni-Mo(w) soportados sobre alúmina: actividad de hidrodesulfuración de tiofeno

    Synthesis and characterization of alumina supported Ni-Mo(w) anderson type heteropolyoxoanions: thiophene hydrodesulfurization activity

    Thumbnail
    Author
    Julio-Julio, Javier José
    Puello-Polo, Esneyder
    Brito, Joaquín
    xmlui.custom.item.dc_identifier
    http://revistas.ustabuca.edu.co/index.php/ITECKNE/article/view/1380
    xmlui.custome.item-addthis
    TY - GEN T1 - Síntesis y caracterización de heteropolioxometalatos tipo anderson de Ni-Mo(w) soportados sobre alúmina: actividad de hidrodesulfuración de tiofeno T1 - Synthesis and characterization of alumina supported Ni-Mo(w) anderson type heteropolyoxoanions: thiophene hydrodesulfurization activity AU - Julio-Julio, Javier José AU - Puello-Polo, Esneyder AU - Brito, Joaquín PB - Universidad Santo Tomás. Seccional Bucaramanga AB - Alumina supported (NH4)4[NiMo6-xWxO24H6]•5H2O Anderson type heteropolyoxometalates were  synthesized  by  coprecipitation.  These  solids  were used  as  precursors  in  the  thiophene hydrodesulfurization  catalytic  at  400  °C. The  catalytic  precursors  were characterized by textural properties (BET specific surface area and, total pore volume and pore diameter distribution),  X-ray  diffraction  (XRD),  IR  spectroscopy  (FTIR) and  S  analysis  (CHON-S).  The specific  surface  area was  between  109  and  35  m2/g  with  total  pore  volume and  pore diameter  distribution  of  0,11-0,34  cm3/g  and 8,9-9,6  nm,  respectively.  XRD showed the presence of NiWO4, (NH4)4[NiMo6O24H6]•5H2O  and  WO3.  FTIR  analysis  can  be  assigned  to  the  characteristic  vibrations  of Anderson-type structure, due to stretching and bending of the functional groups present. The NiMo6-O/Al precursor was the most active in the HDS, it had a conversion of  72,75%  and  was  even  more  active  than  the  AERO commercial  catalyst.  The results of HDS revealed that the catalytic activity increases as follows: NiMo6-O/Al > AERO > NiMo3W3-O/Al > NiW6–O/Al. The catalytic selectivity of precursors and commercial catalyst (AERO) was directed towards the cis-butene. ER - @misc{11634_8389, author = {Julio-Julio Javier José and Puello-Polo Esneyder and Brito Joaquín}, title = {Síntesis y caracterización de heteropolioxometalatos tipo anderson de Ni-Mo(w) soportados sobre alúmina: actividad de hidrodesulfuración de tiofenoSynthesis and characterization of alumina supported Ni-Mo(w) anderson type heteropolyoxoanions: thiophene hydrodesulfurization activity}, year = {}, abstract = {Alumina supported (NH4)4[NiMo6-xWxO24H6]•5H2O Anderson type heteropolyoxometalates were  synthesized  by  coprecipitation.  These  solids  were used  as  precursors  in  the  thiophene hydrodesulfurization  catalytic  at  400  °C. The  catalytic  precursors  were characterized by textural properties (BET specific surface area and, total pore volume and pore diameter distribution),  X-ray  diffraction  (XRD),  IR  spectroscopy  (FTIR) and  S  analysis  (CHON-S).  The specific  surface  area was  between  109  and  35  m2/g  with  total  pore  volume and  pore diameter  distribution  of  0,11-0,34  cm3/g  and 8,9-9,6  nm,  respectively.  XRD showed the presence of NiWO4, (NH4)4[NiMo6O24H6]•5H2O  and  WO3.  FTIR  analysis  can  be  assigned  to  the  characteristic  vibrations  of Anderson-type structure, due to stretching and bending of the functional groups present. The NiMo6-O/Al precursor was the most active in the HDS, it had a conversion of  72,75%  and  was  even  more  active  than  the  AERO commercial  catalyst.  The results of HDS revealed that the catalytic activity increases as follows: NiMo6-O/Al > AERO > NiMo3W3-O/Al > NiW6–O/Al. The catalytic selectivity of precursors and commercial catalyst (AERO) was directed towards the cis-butene.}, url = {} }RT Generic T1 Síntesis y caracterización de heteropolioxometalatos tipo anderson de Ni-Mo(w) soportados sobre alúmina: actividad de hidrodesulfuración de tiofeno T1 Synthesis and characterization of alumina supported Ni-Mo(w) anderson type heteropolyoxoanions: thiophene hydrodesulfurization activity A1 Julio-Julio, Javier José A1 Puello-Polo, Esneyder A1 Brito, Joaquín PB Universidad Santo Tomás. Seccional Bucaramanga AB Alumina supported (NH4)4[NiMo6-xWxO24H6]•5H2O Anderson type heteropolyoxometalates were  synthesized  by  coprecipitation.  These  solids  were used  as  precursors  in  the  thiophene hydrodesulfurization  catalytic  at  400  °C. The  catalytic  precursors  were characterized by textural properties (BET specific surface area and, total pore volume and pore diameter distribution),  X-ray  diffraction  (XRD),  IR  spectroscopy  (FTIR) and  S  analysis  (CHON-S).  The specific  surface  area was  between  109  and  35  m2/g  with  total  pore  volume and  pore diameter  distribution  of  0,11-0,34  cm3/g  and 8,9-9,6  nm,  respectively.  XRD showed the presence of NiWO4, (NH4)4[NiMo6O24H6]•5H2O  and  WO3.  FTIR  analysis  can  be  assigned  to  the  characteristic  vibrations  of Anderson-type structure, due to stretching and bending of the functional groups present. The NiMo6-O/Al precursor was the most active in the HDS, it had a conversion of  72,75%  and  was  even  more  active  than  the  AERO commercial  catalyst.  The results of HDS revealed that the catalytic activity increases as follows: NiMo6-O/Al > AERO > NiMo3W3-O/Al > NiW6–O/Al. The catalytic selectivity of precursors and commercial catalyst (AERO) was directed towards the cis-butene. OL Spanish (121)
    Gestores bibliográficos
    Refworks
    Zotero
    BibTeX
    CiteULike
    Show full item record
    Collections
    • Iteckne [230]
    Abstract
    Alumina supported (NH4)4[NiMo6-xWxO24H6]•5H2O Anderson type heteropolyoxometalates were  synthesized  by  coprecipitation.  These  solids  were used  as  precursors  in  the  thiophene hydrodesulfurization  catalytic  at  400  °C. The  catalytic  precursors  were characterized by textural properties (BET specific surface area and, total pore volume and pore diameter distribution),  X-ray  diffraction  (XRD),  IR  spectroscopy  (FTIR) and  S  analysis  (CHON-S).  The specific  surface  area was  between  109  and  35  m2/g  with  total  pore  volume and  pore diameter  distribution  of  0,11-0,34  cm3/g  and 8,9-9,6  nm,  respectively.  XRD showed the presence of NiWO4, (NH4)4[NiMo6O24H6]•5H2O  and  WO3.  FTIR  analysis  can  be  assigned  to  the  characteristic  vibrations  of Anderson-type structure, due to stretching and bending of the functional groups present. The NiMo6-O/Al precursor was the most active in the HDS, it had a conversion of  72,75%  and  was  even  more  active  than  the  AERO commercial  catalyst.  The results of HDS revealed that the catalytic activity increases as follows: NiMo6-O/Al > AERO > NiMo3W3-O/Al > NiW6–O/Al. The catalytic selectivity of precursors and commercial catalyst (AERO) was directed towards the cis-butene.
     
    Se sintetizaron heteropolioxometalatos tipo Anderson (NH4)4[NiMo6-xWxO24H6]•5H2O soportados sobre γ-Al3O2, utilizando el método de coprecipitación. Estos solidos fueron utilizados como precursores en la reacción de hidrodesulfuración (HDS) de tiofeno a 400°C. Los precursores catalíticos se caracterizaron por propiedades texturales (área específica (B.E.T) y, distribución del diámetro y volumen de poros), difracción de rayos X (DRX), espectroscopía infrarroja (FT-IR) y análisis elemental (CHON-S). Las áreas específicas estuvieron dentro del intervalo de 109 y 35 m2/g con una distribución del diámetro y volumen de poros de 8,9-9,6 nm y 0,11-0,34 cm3/g, respectivamente. El análisis por DRX mostró la presencia de NiWO4, (NH4)4[NiMo6O24H6]•5H2O y WO3. Los análisis FT-IR determinaron la obtención de la estructura tipo Anderson, debido a las distintas flexiones y estiramientos de los grupos funcionales presentes. El precursor NiMo6-O/Al fue el más activo en la HDS, con un porcentaje de conversión de 72,75% e incluso fue más activo que el catalizador comercial AERO. Los resultados de HDS revelaron que la actividad catalítica en HDS se incrementa en el orden: NiMo6-O/Al > AERO > NiMo3W3-O/Al > NiW6–O/Al. La selectividad catalítica de precursores y el catalizador comercial (AERO) estuvo dirigida hacia cis-buteno.
     

     

    xmlui.custome.comments.form-panel-heading

    Respuesta Comentario Repositorio Institucional

    Gracias por tomarse el tiempo para darnos su opinión.

    Indexado por:

    Con presencia en:

    • Bogotá
    • |
    • Bucaramanga
    • |
    • Medellín
    • |
    • Tunja
    • |
    • Villavicencio
    • |
    • Universidad Abierta y a Distancia
    • |
    • Convento Santo Domingo
    Infotegra S.A.S
     

     

    AutoarchivoVideotutorialCarta Aprobación FacultadCarta Derechos de Autor

    Browse

    All of DSpaceCommunities & CollectionsBy Issue DateAuthorsTitlesSubjectsxmlui.ArtifactBrowser.Navigation.browse_sedeThis CollectionBy Issue DateAuthorsTitlesSubjectsxmlui.ArtifactBrowser.Navigation.browse_sede

    My Account

    LoginRegister

    Statistics

    View Usage StatisticsView Google Analytics Statistics

    Indexado por:

    Con presencia en:

    • Bogotá
    • |
    • Bucaramanga
    • |
    • Medellín
    • |
    • Tunja
    • |
    • Villavicencio
    • |
    • Universidad Abierta y a Distancia
    • |
    • Convento Santo Domingo
    Infotegra S.A.S