2025-02-052025-02-05http://hdl.handle.net/11634/63169The intensities of the Raman lines of the ceramic complex (lead titanate) have been investigated as a function of the relation of the areas of the low Raman frequency modes E(1TO) and silent. A change of tetragonal phase into cubic material was observed by Raman spectrjky. The samples were subjected to the same conditions at the time of making the Raman measurements. The UV-vis spectra of absorption suggested a change in energy levels with increasing concentration of lanthanum element (La). This study’s intention is to observe structural changes in the material by means of Raman intensities without using the traditional central position of the peak width in the bands.Las intensidades de las líneas Raman del cerámico complejo (titanato de plomo) se han investigado como una función de la relación de las áreas de los modos Raman de baja frecuencia E (1TO) y silenciosos. Un cambio de fase tetragonal dentro del material cúbico fue observado por espectroscopía Raman. Las muestras fueron sometidas a las mismas condiciones en el momento de realizar las mediciones de Raman. Los espectros UV-vis de absorción sugirieron un cambio en los niveles de energía al aumentar la concentración del elemento de lantano (La). La intención de este estudio es observar cambios estructurales en el material mediante intensidades Raman sin utilizar la posición central tradicional del ancho máximo en las bandas.application/pdfCopyright (c) 2018 ITECKNEEspectroscopía RamanMaterial FerroeléctricoMétodos ÓpticosRaman spectroscopyFerroelectric materialOptical methodsinfo:eu-repo/semantics/article