Villamizar Amaya, Ingrid YadiraPineda Méndez, Ángela MaríaGómez Jiménez, Karen DayanaFernández Carvajal, María Consuelo2024-12-092024-12-092024-11-20Pineda Méndez, A.M., Gómez Jiménez, K.D., Fernández Carvajal, M.C. (2024). Evaluación de la adaptación marginal de incrustaciones en resina compuesta cementadas con cemento resinoso dual y resina precalentada [Tesis de posgrado]. Universidad Santo Tomás, Bucaramanga, Colombiahttp://hdl.handle.net/11634/58823La principal causa de fracaso de las incrustaciones es la microfiltración asociada a la desadaptación marginal que puede asociarse al tipo de cemento utilizado. En el mercado existen múltiples materiales de cementación, sin embargo, su elección ha sido controversial durante los últimos años. Objetivo: evaluar la adaptación marginal de incrustaciones en resina compuesta cementadas con resina precalentada y cemento resinoso dual. Materiales y métodos: se realizó un estudio experimental in vitro utilizando 30 premolares con coronas sanas. Se dividieron en dos grupos iguales (n=15) para la posterior cementación de incrustaciones en resina. Para el grupo 1 se cementaron con resina precalentada (ENA Micerium) y el grupo 2 con cemento resinoso (Duolink, Bisco). Inmediatamente se llevó a cabo una medición del espacio entre la restauración y el diente mediante microscopio electrónico de barrido y se sometieron a termociclaje (10.000 ciclos) simulando envejecimiento de un año. Posteriormente, se repitió el proceso de medición permitiendo la comparación entre estos valores. Resultados: el cemento resinoso presentó una mediana de desadaptación inicial de 86,3 Um y 105,7 Um después de ser sometido al proceso de envejecimiento dando como resultado un mayor deterioro del material en el tiempo a diferencia de la resina precalentada la cual se mantiene más estable, donde la mediana de desadaptación inicial es de 83,2 Um y de 88,3 Um a un año. Conclusiones: la resina precalentada presentó mejores valores de adaptación marginal con respecto al cemento resinoso en el tiempo cero y a un año.The main cause of failure of inlays is microleakage associated with marginal seal, which can be related to the type of cement used. There are multiple types of cements available on the market; however, their choice has been controversial in recent years. Aim: yo evaluate the marginal fit of composite resin inlays cemented with preheated resin and dual-cure resin cement. Materials and Methods: an in vitro experimental study was conducted using 30 premolars with healthy crowns. They were divided into two equal groups (n=15) for the subsequent cementation of resin inlays. Group 1 was cemented with preheated resin (ENA Micerium) and Group 2 with resin cement (Duolink, Bisco). A measurement of the gap between the restoration and the tooth was immediately carried out using a scanning electron microscope, and they were subjected to thermocycling (10,000 cycles) simulating one year of aging. Subsequently, the measurement process was repeated, allowing for a comparison between these values. Results: the resin cement showed a median initial misfit of 86.3 µm and 105.7 µm after being subjected to the aging process, resulting in greater deterioration of the material over time compared to the preheated resin, which remained more stable, with a median initial misfit of 83.2 µm and 88.3 µm after one year. Conclusions: The preheated resin showed better marginal fit values compared to the resin cement at time zero and after one year.application/pdfspaAtribución-NoComercial-SinDerivadas 2.5 Colombiahttp://creativecommons.org/licenses/by-nc-nd/2.5/co/Composite resinResin cementsDental inlayDental marginal adaptationElectron microscope tomografiphycMateriales odontológicosProcedimientos odontológicosRestauraciones odontológicasTrabajo de gradoAbierto (Texto Completo)info:eu-repo/semantics/openAccesshttp://purl.org/coar/access_right/c_abf2Resina compuestaCementos de resinaIncrustación dentalAdaptación marginalTomografía por microscopio electrónicoreponame:Repositorio Institucional Universidad Santo Tomásinstname:Universidad Santo Tomásrepourl:https://repository.usta.edu.co