Rueda, Carlos AlirioMesa Gómez, Bernardo EnriquePérez Rondón, Félix AntonioAránzazu Rincón, JulianaÁvila Duran, Leidy Johana2017-10-032017-10-032017http://hdl.handle.net/11634/9359Objetivo: Determinar la resistencia al volcamiento de coronas en preparaciones que no cumplen con la altura ocluso-cervical requerida de 4mm mediante la realización de las cajuelas en paredes proximales y axiales Materiales y métodos: Se evaluó 100 bloques de acero dividido en 5 grupos, con características de una preparación dental de un molar inferior con altura ocluso – cervical de 3mm, convergencia de 10° y chanfer con angulo interno redondeado, con cajuelas axiales y proximales de 2mm y 3mm de ancho. Se realizó encerado de un molar inferior, escaneo y elaboración de las cofias cobalto cromo con el sistema de sinterización PHIBO. La resistencia de cada muestra se evaluó aplicando fuerzas oblicuas en una angulación de 45 grados, se midió por medio de la maquina universal SHIMADZU. El análisis estadístico entre los grupos evaluados se comparó mediante la prueba de Kruskal-Wallis con un valor p < 0,001 que existe diferencia estadísticamente significativa. Resultados: La cajuela proximal de 3mm de ancho presenta el promedio más bajo con 15058.91, y que los mejores resultados se obtienen con las cajuelas axiales de 2mm y 3mm de ancho presentando el promedio más alto de 18070.94 y 16572.97; dado que presentaron mayor resistencia y no hubo diferencia estadísticamente significativa. Conclusión: Se comprobó que las cajuelas axiales aumentan la resistencia al desalojo de las coronas ante la aplicación de fuerzas oblicuas.Objective: To determine the resistance to crown overturning in preparations that do not meet the required occlusal-cervical height of 4 mm by performing the trunks on proximal and axial walls Materials and methods: 100 steel blocks divided into 5 groups were evaluated, with characteristics of a lower molar tooth preparation with occlusal - cervical height of 3mm, convergence of 10 ° and chanfer with rounded internal angle, with axial and proximal 2mm and 3mm wide. A lower molar was waxed, and the cobalt chromium copings were made with the PHIBO sintering system. The strength of each sample was evaluated by applying oblique forces at 45 degree angulation, measured by the SHIMADZU universal machine. Statistical analysis between the groups evaluated was compared using the Kruskal-Wallis test with a p-value of <0.001, which had a statistically significant difference. Results: The 3mm wide trunk has the lowest average with 15058.91, and the best results are obtained with 2mm and 3mm wide axial trunks with the highest average of 18070.94 and 16572.97; since they presented greater resistance and there was no statistically significant difference. Conclusion: It was verified that the axial bolsters increase the resistance to the eviction of the crowns before the application of oblique forces.application/pdfspaAtribución-NoComercial-SinDerivadas 2.5 Colombiahttp://creativecommons.org/licenses/by-nc-nd/2.5/co/bachelor thesisFixed prosthesis, Dental preparation, Strength, CasingsPrótesisImplantes artificialesCoronas (odontología)Prótesis dentalImplantes dentariosRehabilitación oralDentaduras postizasCoronas odontologíaAbierto (Texto Completo)info:eu-repo/semantics/openAccesshttp://purl.org/coar/access_right/c_abf2Prótesis fijaPreparación dentalResistenciaCajuelasreponame:Repositorio Institucional Universidad Santo Tomásinstname:Universidad Santo Tomásrepourl:https://repository.usta.edu.co