Acevedo Calderón, German HernandoPedraza Álvarez, Rafael LeonardoRuiz Sánchez, Juan Diego2026-02-262026-02-262026-02-26Pedraza Álvarez, R. L. y Ruiz Sánchez, J. D. (2026). Evaluación del uso de cáscara de huevo y carbón de arroz como posible sustituto parcial del agregado fino y cementante en mezclas de mortero no estructural [Trabajo de pregrado]. Universidad Santo Tomás, Bucaramanga, Colombia.http://hdl.handle.net/11634/71795Esta investigación evaluó la factibilidad técnica de incluir desechos agroindustriales como sustitutos parciales del cemento y del agregado fino en morteros no estructurales. Se empleo cascara de huevo (pulverizada y triturada) y carbón de arroz calcinado con el fin de disminuir el uso de materiales convencionales. El objetivo principal fue determinar el impacto de estos reemplazos en el comportamiento mecánico de los cubos de mortero y establecer dosificaciones viables desde un enfoque estructural. Las mezclas se organizaron en cuatro hipótesis con diferentes combinaciones de sustitución, evaluadas mediante ensayos de compresión a los 7, 14 y 28 días conforme a la NTC 3356, y un ensayo de flexión según la ASTM C348 en una viga experimental, Los datos se analizaron mediante métodos estadísticos unifactoriales y multifactoriales para determinar la precisión y confiabilidad de los resultados. Se identificaron seis dosificaciones óptimas (A#11, A#15, B#3, B#7, C#3 y D#2) con resistencias entre 12.5 y 22 MPa, superando la resistencia mínima de un mortero no estructural. El uso moderado de cáscara de huevo mantuvo la resistencia mecánica, mientras que el carbón de arroz actuó favorablemente como adición mineral no reactiva. La mezcla C#3 presentó el mejor desempeño a compresión, demostrando la viabilidad técnica del uso combinado de estos residuos como alternativa sostenible en la fabricación de morteros.This research evaluated thetechnical feasibility of including agro-industrial waste as partial substitutesfor cement and fine aggregate in non-structural mortars. Eggshells (pulverized and crushed) and calcined rice husk charcoal were usedto reduce the use of conventional materials. The main objective wasto determine the impact of these replacements on the mechanical behavior of themortar cubes and to establish viable dosages from a structural approach. The mixtures were organized into four hypotheses with different substitution combinations, evaluated by compression tests at 7, 14, and 28 daysin accordance with NTC 3356, and a flexural test according to ASTM C348 on an experimental beam. Thedata were analyzed using unifactorial and multifactorial statistical methodsto determine the accuracy and reliability of theresults. Six optimal dosages were identified (A#11, A#15, B#3, B#7, C#3, and D#2) with strengths between 12.5 and 22 MPa, exceeding the minimum strength ofa non-structural mortar. The moderate use of eggshell maintained the mechanical strength, while rice husk charcoal acted favorably as a non-reactive mineral additive. The C#3 mixture performed best in compression, demonstrating the technical feasibility of using these wastes in combination as a sustainable alternative in mortar manufacturing.application/pdfspaAttribution-NonCommercial-NoDerivs 2.5 Colombiahttp://creativecommons.org/licenses/by-nc-nd/2.5/co/bachelor thesisNon-structural mortarAgro-Industrial WasteEggshellRice CharcoalCompressive StrengthAnálisis de informaciónAbierto (Texto Completo)info:eu-repo/semantics/openAccesshttp://purl.org/coar/access_right/c_abf2Mortero no estructuralResiduos agroindustrialesCáscara de huevoCarbón de arrozResistencia a compresiónreponame:Repositorio Institucional Universidad Santo Tomásinstname:Universidad Santo Tomásrepourl:https://repository.usta.edu.co