Becerra Buitrago, HernánOrtiz Castro, VickyMéndez Sabogal, Leidy JohanaRojas Rodríguez, Yesica PaolaRomero Hernández, Mónica Liseth2023-06-062023-06-062023-06-05Méndez Sabogal L. J., Rojas Rodríguez, Y. P. Romero Hernández M. L., (2023). Efecto del Xilol sobre la microdureza de la dentina en retratamiento endodóntico. Un estudio piloto in vitro. [Tesis de posgrado]. Universidad Santo Tomás. Bucaramanga, Colombiahttp://hdl.handle.net/11634/50738Antecedente: el uso de disolventes, tales como el Xilol, es frecuente durante el retratamiento endodóntico con el objetivo de facilitar la remoción de la gutapercha. Sin embargo, estos pueden afectar la microdureza y estructura de la dentina. Objetivo: evaluar el efecto del Xilol sobre la microdureza y la estructura química de la dentina luego del retiro de la gutapercha durante el retratamiento endodóntico, en premolares inferiores extraídos por indicación ortodóntica. Materiales y métodos: estudio experimental in vitro, que incluyó 12 dientes premolares unirradiculares extraídos para exodoncia por tratamiento ortodóntico. La muestra fue dividida aleatoriamente en dos grupos, seis para el grupo “control” que correspondió a dientes sin preparación biomecánica y seis para el grupo “expuesto” que correspondió a dientes desobturados con Xilol. Cada diente fue dividido longitudinamente en dirección vestibulolingual. En cada grupo, seis mitades fueron estudiadas con durometro de Vickers (HV) y tres con la espectroscopía de Raman. Resultados: la microdureza de la dentina fue similar entre los dientes sin y con exposición a Xilol, con un promedio reportado en la prueba de Vickers de 55.33.0 HV en el grupo control en comparación de 55.63.0 HV en el grupo expuesto a Xilol. En la prueba de Raman, no se observaron diferencias en la intensidad reportada a lo largo del espectro entre los grupos. En ambos casos, se reportó un pico máximo en 960 cm-1 correspondiente a niveles de hidroxiapatita. Conclusiones: los resultados de este estudio no sugieren cambios en la microdureza y en la estructura química de la dentina debido al uso de Xilol.Introduction: the use of solvents, such as Xylol, is common during endodontic retreatment in order to facilitate gutta-percha removal. However, they can affect dentin microhardness and dentin structure. Objectives: to evaluate the effect of Xylol on dentin microhardness and chemical structure after gutta-percha removal during endodontic retreatment in lower premolars extracted for orthodontic indication. Materials and methods: experimental in vitro study, which included 12 uniradicular premolars extracted for exodontia due to orthodontic treatment. The sample was randomly divided into two groups, six for the "control" group which corresponded to teeth without biomechanical preparation and six for the "exposed" group which corresponded to teeth treated with Xylol. Each tooth was split lengthwise in the vestibulolingual direction. In each group, six halves were studied with Vickers durometer (HV) and three with Raman spectroscopy. Results: dentin microhardness was similar between the teeth without and with Xylol exposure, with an average reported in Vickers test of 55.33.0 HV in the control group compared to 55.63.0 HV in the Xylol group. In the Raman spectroscopy, no differences were observed in the intensity along the spectrum between groups. In both cases, a maximum peak was recorded at 960 cm-1 corresponding to hydroxyapatite levels. Conclusions: the results of this study do not suggest changes in dentin microhardness and chemical structure due to the use of Xylol.application/pdfspaAtribución 2.5 ColombiaAtribución 2.5 Colombiahttp://creativecommons.org/licenses/by/2.5/co/bachelor thesisdentinmicrohardnesschemical structurexylolsolventpulpa dentalcanal radicularcavidad pulpar dentalesmalte dentalAbierto (Texto Completo)info:eu-repo/semantics/openAccesshttp://purl.org/coar/access_right/c_abf2microdurezaxiloldisolventedentinaestructura químicareponame:Repositorio Institucional Universidad Santo Tomásinstname:Universidad Santo Tomásrepourl:https://repository.usta.edu.co