Citotoxicidad del mta y biocerámico sobre células madre de la pulpa dental

Cargando...
Miniatura

Fecha

2018

Enlace al recurso

DOI

ORCID

Google Scholar

Cvlac

gruplac

Descripción Dominio:

Título de la revista

ISSN de la revista

Título del volumen

Editor

Universidad Santo Tomás

Compartir

Documentos PDF
Cargando...
Miniatura

Resumen

Objetivo: Comparar la citotoxicidad del MTA Proroot® y EndoSequence® masilla y pasta, en células madres de pulpa dental humana. Metodología: Estudio experimental In vitro. Las células fueron transportadas en un frasco T75, de la Universidad de Bosque a la Universidad Nacional de Colombia. Las células se sembraron en platos de 6 pozos, que previamente tenían 3mg de cada uno de los materiales. El conteo celular se realizó con un hemocitómetro y azul triphan bajo el microscopio invertido. Los conteos se realizaron a 24, 48 y 72 horas por duplicado. Resultados: Se aplicó la prueba estadística de ANOVA y se encontró que el número de células vivas fue mayor para la masilla a las 24 y 72 horas. En el caso del MTA presentó el menor número de células vivas durante los tiempos de exposición evaluados (24, 48, 72 horas). Conclusión: El material biocerámico es menos citotóxico que el MTA, esto sugiere que es un material seguro para las aplicaciones que implican contacto con tejido adyacente.

Abstract

Objective: to compare the cytotoxicity of MTA Proroot® and EndoSequence® putty and paste, in human dental pulp stem cells. Methodology: In vitro experimental study. The cells were transported in a T75 bottle, from the Universidad del Bosque to the National University of Colombia. The cells were seeded in 6-well plates, which previously had 3mg of each of the materials. The cell count was performed with a hemocytometer and triphan blue under the inverted microscope. The counts were made at 24, 48 and 72 hours in duplicate. Results: The ANOVA statistical test was applied and it was found that the number of living cells was greater for the putty at 24 and 72 hours. In the case of the MTA presented the lowest number of living cells during the exposure times evaluated (24, 48, 72 hours). Conclusion: The bioceramic material is less cytotoxic than MTA, this is a safe material for applications that involve contact with adjacent tissue.

Idioma

spa

Palabras clave

Citación

Peñate Salcedo, C. A. Rodríguez Merchán, O. Sandoval Castillo, F. A. (2018). Citotoxicidad del mta y biocerámico sobre células madre de la pulpa dental. [Trabajo de Especialización]. Universidad Santo Tomás, Bucaramanga, Colombia.

Licencia Creative Commons

Atribución-NoComercial-SinDerivadas 2.5 Colombia