Resistencia compresiva de tres materiales para elaborar placas oclusales, sometidos o no a un proceso de envejecimiento acelerado. Estudio in vitro.
Cargando...
Fecha
2024-11-26
Director
Enlace al recurso
DOI
ORCID
Google Scholar
Cvlac
gruplac
Descripción Dominio:
Título de la revista
ISSN de la revista
Título del volumen
Editor
Universidad Santo Tomás
Compartir
Documentos PDF
Cargando...
Resumen
Introducción. Los tratamientos no invasivos más utilizados para los trastornos temporomandibulares debido a su seguridad y comodidad son las férulas oclusales. Estos dispositivos se pueden elaborar en diferentes materiales ofrecidos en el mercado. Objetivo. Determinar la resistencia a la fractura de tres materiales utilizados para elaborar placas oclusales sometidos o no a un ciclo de envejecimiento acelerado de 6 meses. Métodos. Se escogieron 3 materiales utilizados para realizar férulas oclusales. En total se usaron 54 láminas, 18 de cada material (acrílico de autocurado, resina Prizma 3D bio Splint LCD y Erkoloc), 9 unidades de cada grupo se sometieron a proceso de envejecimiento acelerado por medio de la máquina “BEGO hygrotherm” por un ciclo de 6 meses (27 láminas), posteriormente, todas las láminas fueron sometidas a fuerzas compresivas por medio de la máquina Instrom, donde se evaluó el tiempo de máxima deformación en segundos, máxima deformación en milímetros y fuerza alcanzada en kilonewtons. Finalmente, las láminas se observaron en estereomicroscopio para verificar alteraciones en la superficie. Resultados. El comportamiento de los materiales presentó diferencias estadísticas significativas en las variables evaluadas (tiempo, material, resistencia, fuerza compresiva, envejecimiento acelerado y desplazamiento) excepto en la fuerza necesaria para generar la máxima deformación después del proceso de envejecimiento, en donde no se observaron diferencias significativas. Se evidencia que “Erkoloc” es el material que presenta mayores deformaciones con menor fuerza y mayor tiempo para lograrlas, lo que se interpreta como un material más moldeable y deformable, pero esa capacidad se pierde un poco, después del envejecimiento. Las láminas elaboradas con resina acrílica tenían más burbujas al ser observadas en estereomicroscopio y defectos superficiales fueron observados en todas las láminas de distintos materiales tanto en los sometidos a envejecimiento, como los que no. Conclusión: Ningún material llegó a la fractura y el más resistente fue el acrílico de autocurado.
Abstract
Introduction: The most used non-invasive treatments for temporomandibular disorders due to their safety and convenience are occlusal splints. These devices can be made from various materials available on the market. Objective: To determine the fracture resistance of three materials used for fabricating occlusal splints, either subjected to or not subjected to an accelerated aging cycle of 6 months. Methods: Three materials commonly used for making occlusal splints were selected: Prizma 3D bioSplint LCD resin, self-curing acrylic, and Erkoloc. The splints were divided into two groups: the first group consisted of splints subjected to compressive forces using the Instron machine, and the second group consisted of splints subjected to compressive forces plus accelerated aging. A total of 54 splints of different materials were used, with 18 units each of the 3 types (self-curing acrylic, Prizma 3D bioSplint LCD resin, and Erkoloc). Nine units were subjected to accelerated aging using the BEGO hygrotherm machine for a 6-month cycle (27 splints). Subsequently, all 54 splints were subjected to compressive forces using the Instron machine, where the maximum deformation time in seconds, maximum deformation in millimeters, and force achieved in kilonewtons were evaluated. Finally, the splints were examined under a stereomicroscope to check for surface alterations. Results: The materials exhibited statistically significant differences in the evaluated variables (time, force), except in the force required to achieve maximum deformation after the aging process, where no significant differences were observed. It was found that Erkoloc is the material that exhibited the greatest deformations with less force and longer time to achieve them, indicating a more moldable and deformable material, though this capability is somewhat reduced after aging. The splints made from acrylic resin had more bubbles when observed under the stereomicroscope, and surface defects were observed in all splints of different materials, both those subjected to aging and those that were not.
Idioma
spa
Palabras clave
Citación
Cárdenas Rodríguez, J. T., Rodríguez García, S. A., Ramírez Bonilla, J. A., & Medina, D. M. (2024). Resistencia compresiva de tres materiales para elaborar placas oclusales, sometidos o no a un proceso de envejecimiento acelerado. Estudio in vitro. [Tesis de posgrado] Universidad Santo Tomás, Bucaramanga.